| Analysis | Unit | Limit | Test Method |
| Density @ 25°C | kg/m3 | 1000-1050 | ASTM D70 or D3289 |
| Penetration @ 25°C | mm/10 | 120-150 | ASTM D5 |
| Softening point | °C | 37 min | ASTM D36 |
| Ductility @ 25°C | cm | 100 min | ASTM D113 |
| Loss on heating | wt% | 0.5 max | ASTM D6 |
| Drop in penetration after heating | % | 20 max | ASTM D5 |
| Flash point | °C | 220 min | ASTM D92 |
| Solubility in Trichloroethylene | wt% | 99.0 min | ASTM D2042 |
| Spot test | Negative | AASHTO T102 | |
| Dynamic Viscosity @ 60°C | Pa.S | 45 | ASTM D2171 |
| Kinematic Viscosity @ 135°C | cSt | 170 min | ASTM D2170 |
| Wax Content | % | 2 max | DIN EN 12606-1 |
| Retained Penetration after (T.F.O.T). % | % | 42 min | ASTM D5 |
| Ductility, (25°C), 5cm/min, cm after TFOT | cm | 100 min | ASTM D113 |
| Viscosity @ 60°C | Pa.S | 225 max | ASTM D2171 |